High Alumina Refractory Brick
In China, according to the content of Al2O3 in high alumina refractory bricks , it is usually pided into three grades: Grade IAl2O3 content75%; Grade IIAl2O3 content is 60-75%; Grade IIIAl2O3 content is 48-60%. The production process of high-alumina bricks and multi-clinker clay bricks is similar, the difference is that the proportion of clinker in the ingredients is higher, which can be as high as 90-95%. Higher, such as I, II and other high alumina bricks are generally 1500 ~ 1600 ℃ when fired in tunnel kilns. Feature 1. Refractoriness The refractoriness of high alumina refraactory bricks i
Composition: Premium materials such as high alumina oxide, magnesium oxide, and silicon carbide, with customizable composition based on client requirements.
Form: Available in powder, brick, board, and castable forms to suit various application needs.
Refractoriness: Standard range from 1200°C to 1800°C, with options for higher temperature customization.
Application Fields: Widely used in industries such as steel, cement, glass, and petrochemicals for furnace lining and insulation.
Packaging: Options include 25 kg bags, bulk bags, and custom packaging solutions compliant with global transportation standards.
Introduction
Our experienced R&D team can customize the material, form, and size according to your specific application needs while ensuring compliance with international quality standards. With rigorous quality control and advanced production facilities, we guarantee products with high refractoriness, excellent compressive strength, and long-lasting durability. Whether you are in the steel, cement, glass, or petrochemical industry, we are your trusted partner, supporting the success of your projects.
For customization inquiries, please feel free to contact us. We will provide tailor-made solutions based on your requirements.
High Alumina Refractory Brick Details
In China, according to the content of Al2O3 in high alumina refractory bricks, it is usually pided into three grades: Grade I——Al2O3 content>75%; Grade II——Al2O3 content is 60-75%; Grade III——Al2O3 content is 48-60%.
The production process of high-alumina bricks and multi-clinker clay bricks is similar, the difference is that the proportion of clinker in the ingredients is higher, which can be as high as 90-95%. Higher, such as I, II and other high alumina bricks are generally 1500 ~ 1600 ℃ when fired in tunnel kilns.
Feature
1. Refractoriness
The refractoriness of high alumina refraactory bricks is higher than that of clay bricks and semi-silica bricks, reaching 1750~1790℃, which belongs to advanced refractory materials.
2. Load softening temperature
Because the Al2O3 in high alumina products is high, the amount of impurities is low, and the fusible glass body is less, so the softening temperature under load is high, but because the mullite crystal does not form a network structure, the softening temperature under load is still not as high as that of silica brick.
3. Slag resistance
High alumina refractory bricks are close to neutral refractory materials and can resist the erosion of acidic slag and alkaline slag. Because they contain SiO2, their ability to resist alkaline slag is weaker than that of acid-resistant slag.
Application
Mainly used for masonry blast furnace, hot blast stove, electric furnace roof, blast furnace, reverberatory furnace, rotary kiln lining. In addition, high alumina bricks are also widely used as open hearth regenerative checker bricks, plugs for pouring systems, nozzle bricks, etc.
Physical And Chemical Indicators
|
Brand Properties |
SK-40 |
SK-38 |
SK-37 |
SK-36 |
SK-35 |
|
|
Refractoriness (SK) |
40 |
38 |
37 |
36 |
35 |
|
|
Apparent Porosity (%) |
22 |
23 |
23 |
23 |
23 |
|
|
Bulk Density (g/cm3) |
2.65 |
2.40 |
2.35 |
2.30 |
2.25 |
|
|
Cold Crushing Strength(MPa) |
70 |
52 |
50 |
45 |
40 |
|
|
Thermal Linear Expansion(%) @1000deg |
0.6 |
0.6 |
0.6 |
0.6 |
0.6 |
|
|
Permanent Linear Change(%) @1400degx2hrs |
±0.2 |
±0.3 |
±0.3 |
±0.3 |
±0.3 |
|
|
Refractoriness under Load (ºC) @0.2MPa |
1,530 |
1,500 |
1,450 |
1,420 |
1,380 |
|
|
Chemical Composition(%) |
Al2O3 |
80 |
72 |
60 |
50 |
45 |
|
Fe2O3 |
1.8 |
2.0 |
2.0 |
2.0 |
2.0 |
|