The water absorption rate of the selected first-grade high-alumina clinker is less than 5%, and the second-grade high-alumina clinker is less than 7%. Then, the soft clay and bauxite clinker with a water content of less than 4% are mixed and finely ground. Using this mixed fine grinding powder ingredients can reduce the porosity of the brick.

The particle gradation during batching, the ratio of coarse to fine is 4:2:4, and the large particles should not exceed 5mm. The order of addition during mixing is as follows: firstly add coarse particles, then add sulfite pulp waste liquid, premix for 3 minutes, and then add high aluminum fine powder for mixing. It is strictly forbidden to add coarse and fine particles to the mill and add sulfurous acid pulp waste liquid at the same time.

In order to reduce the porosity of special alumina bricks, the single-sided pressure is changed to double-sided pressure to double-sided pressure, and the number of blows varies according to the amount of feed. If it is fired by inverted flame kiln, the position of the fire-absorbing hole should be adjusted so that the middle is dense and the edges are thin, and it is properly encrypted near the kiln door, so that the temperature difference between the upper and lower kilns, and the temperature difference between inside and outside are not more than 20 degrees.

Features

Good performance in high temp refractoriness under load

Higher temperate resistant with good refractoriness

Lower impurity content

Good thermal shock resistance performance

Excellent resistance in slag abrasion

Good cold crush strength

Applications

Lime Kiln Cement Kiln

Various Rotary kiln

Glass melting Tank

Electric Arc Furnace

Blast Furnace

Chamber Combustor

Nonferrous Metal Furnace

Various high-temp Furnace

Specifications

SPecial-alumina refractory birck

JUCOS Alumina contents range from 60% to 80%

Widely used throughout metallurgical industry

Physical And Chemical Indicators